Other alloy powder
Powder Technical Parameter Specification Application
KF-Mo HRC¡«20
Working Temperature: Max. 350¡æ
Mo 99.5%		 Exothermal spray powder. High bonding strength. Good wear resistance. Plasma Spraying
Good for piston ring.
KF-Ag Ag The same corrosion resistance property as fine silver. Good acid, alkali and salt erosion resistance properties. Plasma Spraying
Good for aviation parts.
KF-350 Ag:70.5-73.5 Cu(Bal.) Silver Copper alloy powder. Good toughness and high temperature anti-glue properties. Plasma Spraying
Used as wear reducing sealing coating or braze welding materials.
KF-Al Al99 Special pure Aluminum powder for spraying.
Non-magnetic coating.
Good electric conduction, thermal conduction and shielding radio-wave properties.		 Flame spraying
Plasma Spraying
Spraying Aluminum coating to protecting parts.
KF-340 Working Temperature: Max. 400¡æ
Si 12 Al 18		 Aluminum alloy powder with 12 percent silicon content.
Denser than pure Aluminum spraying coating.
Used as storing parts of Aluminum, Aluminum alloy and Magnesium alloy. Easy to cut. Have good smoothness.		 Flame spraying
Plasma Spray
Restoring Aluminum alloy surface.
Spraying and filling Aluminum alloy casting parts.
KF-117 Working Temperature: ¡Ü400-600¡æ
Ni 25 Cu 57 Al 6.4 Cg(Bal.) 		Copper Aluminium Nickel Graphite powder.
Low friction coating material.
Good self-lubricating and toughness properties. 		Flame spraying
Plasma Spray
Good for compressor parts of aircraft engine.
KF-116 Working Temperature: ¡Ü400-600¡æ
Ni Cr Al Cg 		Nickel Chromium Aluminium Graphite powder.
Low friction, good self-lubricating, wear reducing properties.		 Flame spraying
Plasma Spray
Good for compressor parts of aircraft engine.
Copyright:SMM,Beijing General Research Institute of Mining & Metallurgy
Add: 1.Wenxing St., Xizhimenwai Beijing, 100044, China
Tel: 0086-10-68324908,0086-10-68333366-2803,0086-10-68333366-2014 Fax:0086-10-88385389
E£­mail:bjmetal@bbn.cn